Mg-based hydride is a promising hydrogen storage material, but its capacity is hindered by the kinetic properties. In this study, Mg–Mg₂Ni–LaH_x nanocomposite is formed from the H-induced decomposition of Mg₉₈Ni_1·67La_0.33 alloy. The hydrogen capacity of 7.19 wt % is reached at 325 °C under 3 MPa H₂, attributed to the ultrahigh hydrogenation capacity in Stage I. The hydrogen capacity of 5.59 wt % is achieved at 175 °C under 1 MPa H₂. The apparent activation energies for hydrogen absorption and desorption are calculated as 57.99 and 107.26 kJ/mol, which are owing to the modified microstructure with LaH_x and Mg₂Ni nanophases embedding in eutectic, and tubular nanostructure adjacent to eutectic. The LaH_2.49 nanophase can catalyze H₂ molecules to dissociate and H atoms to permeate due to its stronger affinity with H atoms. The interfaces of these nanophases provide preferential nucleation sites and alleviate the “blocking effect” together with tubular nanostructure by providing H atoms diffusion paths after the impingement of MgH₂ colonies. Therefore, the superior hydrogenation properties are achieved because of the rapid absorption process of Stage I. The efficient synthesis of nano-catalysts and corresponding mechanisms for improving hydrogen storage properties have important reference to related researches.     

Performance of BaZrO3/Y2O3 dual-phase refractory applied to TiAl alloy melting

Vacuum induction melting is a potential process for the preparation of TiAl alloys with good homogeneity and low cost. But the crucial problem is a selection of high stability refractory. In this study, a BaZrO₃/Y₂O₃ dual-phase refractory was prepared and its performance for melting TiAl alloys was studied and compared with that of a Y₂O₃ refractory. The results showed the dual-phase refractory consisted of BaZr_1-xY_xO_3-δ and Y₂O₃(ZrO₂), exhibited a thinner interaction layer (30 μm) than the Y₂O₃ refractory (90 μm) after melting the TiAl alloy. Although the TiAl alloys melted in the dual-phase and Y₂O₃ refractory exhibited similar oxygen contamination (<0.1 wt%), the alloy melted in the dual-phase refractory had smaller Y₂O₃ inclusion content and size than that in the Y₂O₃ refractory, indicating that the dual-phase refractory exhibited a better melting performance than the Y₂O₃ refractory. This study provides insights into the process of designing highly stable refractory for melting TiAl alloys.     

Nickel‒cobalt bimetallic catalysts prepared from hydrotalcite-like compounds for dry reforming of methane

Ni–Co/Mg(Al)O alloy catalysts with different Co/Ni molar ratios have been prepared from Ni- and Co-substituted Mg–Al hydrotalcite-like compounds (HTlcs) as precursors and tested for dry reforming of methane. The XRD characterization shows that Ni–Co–Mg–Al HTlcs are decomposed by calcination into Mg(Ni,Co,Al)O solid solution, and by reduction finely dispersed alloy particles are formed. H₂-TPR indicates a strong interaction between nickel/cobalt oxides and magnesia, and the presence of cobalt in Mg(Ni,Co,Al)O enhances the metal-support interaction. STEM-EDX analysis reveals that nickel and cobalt cations are homogeneously distributed in the HTlcs precursor and in the derived solid solution, and by reduction the resulting Ni–Co alloy particles are composition-uniform. The Ni–Co/Mg(Al)O alloy catalysts exhibit relatively high activity and stability at severe conditions, i.e., a medium temperature of 600 °C and a high space velocity of 120000 mL g^?1 h^?1. In comparison to monometallic Ni catalyst, Ni–Co alloying effectively inhibits methane decomposition and coke deposition, leading to a marked enhancement of catalytic stability. From CO₂-TPD and TPSR, it is suggested that alloying Ni with Co favors the CO₂ adsorption/activation and promotes the elimination of carbon species, thus improving the coke resistance. Furthermore, a high and stable activity with low coking is demonstrated at 750 °C. The hydrotalcite-derived Ni–Co/Mg(Al)O catalysts show better catalytic performance than many of the reported Ni–Co catalysts, which can be attributed to the formation of Ni–Co alloy with uniform composition, proper size, and strong metal-support interaction as well as the presence of basic Mg(Al)O as support.     

Development of a H2-permeable Pd60Cu40-based composite membrane using a reverse build-up method

A new reverse build-up method is developed to fabricate an economical H₂-permeable composite membrane. Sputtering and electroplating are used for the formation of a membrane comprised of a 3.7-μm-thick Pd₆₀Cu₄₀ (wt.%) alloy layer and a 13-μm-thick porous Ni support layer, respectively. The H₂-permeation measurements are performed under the flow of a gaseous mixture of H₂ and He at 300–320 °C and 50–100 kPa of H₂ partial pressure. The H₂/He selectivity values exceed 300. The activation energy at 300–320 °C is 10.9 kJ mol⁻¹. The H₂ permeability of the membrane is 1.25 × 10⁻⁸ mol m⁻¹ s⁻¹ Pa^−0.5 at 320 °C after 448 h. The estimated Pd cost of the proposed membrane is approximately 1/8 of the cost for a pure Pd₆₀Cu₄₀ membrane. This study demonstrates that the proposed method allows the facile production of low-cost, Pd-based membranes for H₂ separation.     

Bifunctional nanoporous ruthenium-nickel alloy nanowire electrocatalysts towards oxygen/hydrogen evolution reaction

A class of ruthenium-nickel alloy catalysts featured with nanoporous nanowires (NPNWs) were synthesized by a strategy combining rapid solidification with two-step dealloying. RuNi NPNWs exhibit excellent electrocatalytic activity and stability for oxygen evolution reaction (OER) and hydrogen evolution reaction (HER) in which the RuNi-2500 NPNWs catalyst shows an OER overpotential of 327 mV to deliver a current density of 10 mA cm^?2 and the RuNi-0 NPNWs catalyst requires the overpotential of 69 mV at 10 mA cm^?2 showing the best HER activity in alkaline media. Moreover, the RuNi-1500 NPNWs catalyst was used as the bifunctional electrocatalyst in a two-electrode alkaline electrolyzer for water splitting, which exhibits a low cell voltage of 1.553 V and a long-term stability of 24 h at 10 mA cm^?2, demonstrating that the RuNi NPNWs catalysts can be considered as promising bifunctional alkaline electrocatalysts.     

Interfacial microstructure and mechanical properties of Ti3SiC2 ceramic and TC11 alloy joint diffusion bonded with a Cu interlayer

Reliable joints of Ti₃SiC₂ ceramic and TC11 alloy were diffusion bonded with a 50 μm thick Cu interlayer. The typical interfacial structure of the diffusion boned joint, which was dependent on the interdiffusion and chemical reactions between Al, Si and Ti atoms from the base materials and Cu interlayer, was TC11/α-Ti + β-Ti + Ti₂Cu + TiCu/Ti₅Si₄ + TiSiCu/Cu(s, s)/Ti₃SiC₂. The influence of bonding temperature and time on the interfacial structure and mechanical properties of Ti₃SiC₂/Cu/TC11 joint was analyzed. With the increase of bonding temperature and time, the joint shear strength was gradually increased due to enhanced atomic diffusion. However, the thickness of Ti₅Si₄ and TiSiCu layers with high microhardness increased for a long holding time, resulting in the reduction of bonding strength. The maximum shear strength of 251 ± 6 MPa was obtained for the joint diffusion bonded at 850 °C for 60 min, and fracture primarily occurred at the diffusion layer adjacent to the Ti₃SiC₂ substrate. This work provided an economical and convenient solution for broadening the engineering application of Ti₃SiC₂ ceramic.     

Inconel 690传热管GTAW对接焊接头组织及力学性能研究

对Inconel 690传热管材进行钨极气体保护焊(GTAW)对接焊,采用拉伸试验机、压扁试验机和光学显微镜测试和分析传热管焊接接头,同时利用ANSYS软件开展焊接接头在设计工况失压时的一次应力强度校核。研究结果表明:焊缝中心为树枝胞状晶,熔合线附近为粗大柱状晶。室温时接头的平均抗拉强度为619 MPa,平均屈服强度为292 MPa,350℃时接头平均抗拉强度为475 MPa,平均屈服强度为206 MPa,拉伸接头断裂从熔合区开始贯穿整个焊缝组织,呈塑性断裂。压扁试验和反向压扁试验结果表明管接头完好。通过ANSYS分析可知,设计工况下传热管接头350℃许用应力强度150 MPa限值可满足其一次应力强度要求,且裕量较大。     

Designing amorphous formulations of polyphenols with naringin by spray-drying for enhanced solubility and permeability

Naringin (NAR), a major flavanone (FVA) glycoside, is a component of food mainly obtained from grapefruit. We used NAR as a food additive to improve the solubility and permeability of hydrophobic polyphenols used as supplements in the food industry. The spray-dried particles (SDPs) of NAR alone show an amorphous state with a glass transition temperature (T_g) at 93.2 °C. SDPs of hydrophobic polyphenols, such as flavone (FVO), quercetin (QCT), naringenin (NRG), and resveratrol (RVT) were prepared by adding varying amounts of NAR. All SDPs of hydrophobic polyphenols with added NAR were in an amorphous state with a single T_g, but SDPs of hydrophobic polyphenols without added NAR showed diffraction peaks derived from each crystal. The SDPs with NAR could keep an amorphous state after storage at a high humidity condition for one month, except for SDPs of RVT/NAR. SDPs with NAR enhanced the solubility of hydrophobic polyphenols, especially NRG solubility, which was enhanced more than 9 times compared to NRG crystal. The enhanced solubility resulted in the increased membrane permeability of NRG. The antioxidant effect of the hydrophobic NRG was also enhanced by the synergetic effect of NAR. The findings demonstrated that NAR could be used as a food additive to enhance the solubility and membrane permeability of hydrophobic polyphenols.     

The influence of FeNi nanoparticles on the microstructures and soft magnetic properties of FeSi soft magnetic composites

In this work, a new type of FeSi/FeNi soft magnetic powder core (SMPC) was successfully fabricated by coating FeNi nanoparticles on the surface of FeSi micrometer powder. The effects of different contents of FeNi nanoparticles on the micromorphology, internal structures, and soft magnetic properties of SMPCs were studied. The results show that FeNi nanoparticles adhere to the surface of FeSi powder, which can effectively fill the air gap between FeSi powder and is beneficial to the compaction of the powder cores during the pressing process. Thus, the density of the SMPCs is increased. Compared to FeSi SMPCs, the comprehensive soft magnetic properties of FeSi/FeNi SMPCs have been greatly improved. When adding 15 wt% FeNi nanoparticles, the SMPCs exhibit excellent magnetic properties with high effective permeability (increased by 43.8 %) and low core loss (decreased by 22.1 %). The high performance FeSi/FeNi SMPCs prepared in this work are expected to be widely used in power choke coils, uninterruptible power supplies, and boosts and inverter inductors.